E308L-16

E308L-16
Product name : E308L-16
Item : A002
Details :
 

A002

According with GB E308L-16
Corresponding with AWS  E308L-16


Introduction: A002 is a kind of ultra-low-carbon Cr19Ni10 stainless steel electrode with lime-titania type coating. The carbon content of the deposited metal is lower than or equal to 0.04%. It has excellent intercrystalline corrosion-resistance and welding performance. The coating has red-resistance, high strength and good blowhole-resistance. AC/DC.


Uses: Used for welding ultra-low-carbon Cr19Ni10 stainless steel structures, and also used for 0Cr19Ni11Ti corrosion-resistant stainless steel structures whose working temperature is lower than 300℃. Mainly used for the production of equipment of synthetic fiber, chemical fertilizers, petroleum, etc.


Chemical Composition of Deposited Metal (%)
Chemical Composition
C
Mn
Si
S
P
Cu
Ni
Mo
Cr
Guarantee Value
≤0.04
0.5~2.5
≤0.90
≤0.030
≤0.040
≤0.75
9.0~11.0
≤0.75
18.0~21.0

Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
A(%)
Guarantee Value
≥520
≥35

Reference Current (AC, DC+)
Electrode Diameter(mm)
φ2.0
φ2.5
φ3.2
φ4.0
φ5.0
Welding Current (A)
40~80
50~100
70~130
100~160
140~200

Instructions:
1.The electrodes should be baked under 200-250℃ for an hour before welding.
2.Direct current had better be used and the current should not be too strong.
[Next : A902]→
Related Products :
E2209-15
JQ.S2215
E2209-15
E312-16
A1002
E312-16
E430-16
G302
E430-16
E410-16
G202
E410-16
E316-16
A201
E316-16
E317-16
A242
E317-16
E320-16
A902
E320-16