E316-16

E316-16
Product name : E316-16
Item : A201
Details :
 

A201

According with GB E316-16
Corresponding with AWS  E316-16


Introduction: A201 is a kind of low-carbon Cr18Ni12Mo2 stainless steel electrode with titania type coating. When welding, the coating does not turn red or crack due to Mo added to the weld metal. It has excellent corrosion-resistance, heat-resistance and crack-resistance, especially suitable for chloride ion pitting corrosion-resistance. AC/DC.


Uses: Used for welding 0Cr18Ni12Mo2 stainless steel equipment working in organic acid and mineral acid (non-oxidizing acid) medium, and also used for welding high-chrome steel, which can not be given heat treatment after welding, and dissimilar steel.


Chemical Composition of Deposited Metal (%)
Chemical Composition
C
Mn
Si
S
P
Cu
Ni
Mo
Cr
Guarantee Value
≤0.08
0.5~2.5
≤0.90
≤0.030
≤0.040
≤0.75
11.0~14.0
2.00~3.00
17.0~20.0

Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
A(%)
Guarantee Value
≥520
≥30

Reference Current (AC, DC+)
Electrode Diameter(mm)
φ2.0
φ2.5
φ3.2
φ4.0
φ5.0
Welding Current (A)
40~80
50~100
70~120
90~160
160~200

Instructions:
1.The electrodes should be baked under about 250℃ for an hour before welding.
2.Direct current had better be used and the current should not be too strong.
←[Previous : A242] [Next : G202]→
Related Products :
E2209-15
JQ.S2215
E2209-15
E312-16
A1002
E312-16
E430-16
G302
E430-16
E410-16
G202
E410-16
E317-16
A242
E317-16
E320-16
A902
E320-16
E308L-16
A002
E308L-16