E410-16

E410-16
Product name : E410-16
Item : G202
Details :
 

G202

According with GB E410-16
Corresponding with AWS  E410-16


Introduction: G202 is a kind of Cr13 stainless steel electrode with lime-titania type coating. AC/DC.


Uses: Used for welding 0Cr13 and 1Cr13 stainless steel structures, and also used for corrosion-resistant and wear-resistant surface overlaying.


Chemical Composition of Deposited Metal (%)
Chemical Composition
C
Mn
Si
S
P
Cu
Ni
Mo
Cr
Guarantee Value
≤0.12
≤1.00
≤0.90
≤0.030
≤0.040
≤0.75
≤0.70
≤0.75
11.0~13.5

Mechanical Properties of Deposited Metal
 (The temperature of the test pieces should be preserved under 730-760℃ for an hour, and then they should be cooled along with the furnace to 315℃ at a speed of not higher than 60℃/h, and finally cooled in the air.)
Test Item
Rm(MPa)
A(%)
Guarantee Value
≥450
≥20

Reference Current (AC, DC+)
Electrode Diameter(mm)
φ2.0
φ2.5
φ3.2
φ4.0
φ5.0
Welding Current (A)
40~80
50~100
70~130
100~160
140~200

Instructions:
1.The electrodes must be baked under about 150℃ for an hour before welding.
2.The weldments should be preheated to 250-350℃ before welding, and tempered under 700-730℃ after welding.
←[Previous : A201] [Next : G302]→
Related Products :
E2209-15
JQ.S2215
E2209-15
E312-16
A1002
E312-16
E430-16
G302
E430-16
E316-16
A201
E316-16
E317-16
A242
E317-16
E320-16
A902
E320-16
E308L-16
A002
E308L-16