E430-16

E430-16
Product name : E430-16
Item : G302
Details :
 

G302

According with GB E430-16
Corresponding with AWS  E430-16


Introduction: G302 is a kind of Cr17 stainless steel electrode with titania type coating. AC/DC.


Uses: Used for welding nitric acid corrosion-resistant and heat-resistant Cr17 stainless steel structures.


Chemical Composition of Deposited Metal (%)
Chemical Composition
C
Mn
Si
S
P
Cu
Ni
Mo
Cr
Guarantee Value
≤0.10
≤1.00
≤0.90
≤0.030
≤0.040
≤0.75
≤0.60
≤0.75
15.0~18.0

Mechanical Properties of Deposited Metal
 (The temperature of the test pieces should be preserved under 760-790℃ for an hour, and then they should be cooled along with the furnace to 595℃ at a speed of not higher than 55℃/h, and finally cooled in the air.)
Test Item
Rm(MPa)
A(%)
Guarantee Value
≥450
≥20

Reference Current (AC, DC+)
Electrode Diameter(mm)
φ2.0
φ2.5
φ3.2
φ4.0
φ5.0
Welding Current (A)
40~80
50~100
70~130
100~160
140~200

Instructions:
1.G302 electrodes must be baked under about 250℃ for an hour before welding.
2.The weldments should be preheated to 200℃ before welding, and tempered under 750-800℃ after welding.
3.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before welding.
←[Previous : G202] [Next : A1002]→
Related Products :
E2209-15
JQ.S2215
E2209-15
E312-16
A1002
E312-16
E410-16
G202
E410-16
E316-16
A201
E316-16
E317-16
A242
E317-16
E320-16
A902
E320-16
E308L-16
A002
E308L-16