E7015-A1

E7015-A1
Product name : E7015-A1
Item : R107
Details :
 

R107

According with GB E5015-A1
Corresponding with AWS  E7015-A1


Introduction: R107 is a kind of Mo0.5% pearlitic heat-resistant steel electrode with low-hydrogen type coating. DCRP (Direct Current Reversed Polarity). All-position welding. The weldments should be given preheating and postweld heat treatment according to their structural features.


Uses: Used for welding boiler pipes below 510℃ (such as 15Mo). Also used for welding general low-alloy high strength steel.


Chemical Composition of Deposited Metal (%)
Chemical Composition
C
Mn
Si
S
P
Mo
Guarantee Value
0.05~0.12
≤0.90
≤0.60
≤0.035
≤0.035
0.40~0.65

Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReL或Rp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥490
≥390
≥22
≥47(normal temperature)
General Result
490~590
≥400
≥22
≥60

Diffusible Hydrogen Content in Deposited Metal: ≤6.0ml/100g(Glycerine Hydrogen Test)

X-ray Radiographic Inspection: ⅠDegree

Reference Current (DC+)
Electrode Diameter(mm)
φ2.0
φ2.5
φ3.2
φ4.0
φ5.0
Welding Current (A)
40~70
60~90
90~120
140~180
170~210

Instructions:
1.The electrodes must be baked under about 350℃ for an hour before welding, and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before welding.
←[Previous : R207] [Next : R106Fe]→
Related Products :
E7018-A1
R106Fe
E7018-A1
E8015-B1
R207
E8015-B1
E8018-B2
R306Fe
E8018-B2
E8015-B2
R307
E8015-B2
E8015-B2E9015-B3
R407
E8015-B2E9015-B3