E7018

E7018
Product name : E7018
Item : J506Fe
Details :
 

J506Fe

According with GB E5018
Corresponding with AWS  E7018


Introduction: J506Fe is a kind of carbon steel electrode with iron powder low-hydrogen potassium type coating. AC/DC. The deposition efficiency can be improved due to the iron powder in the coating. It has stable arc, fewer spatters, good slag detachability and excellent welding performance. The deposited metal has excellent mechanical properties. All-position welding.


Uses: Used for welding carbon steel and low-alloy steel structures, such as 16Mn, etc.


Chemical Composition of Deposited Metal (%)
Chemical Composition
C
Mn
Si
S
P
Ni
Mo
Cr
V
Guarantee Value
≤0.12
≤1.60
≤0.75
≤0.035
≤0.040
≤0.30
≤0.30
≤0.20
≤0.08

Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReL(Mpa)
A(%)
KV2(J)
Guarantee Value
≥490
≥400
≥22
≥27(-30℃)
General Result
520~580
≥410
24~30
80~200

Diffusible Hydrogen Content in Deposited Metal: ≤8.0ml/100g(Glycerine Hydrogen Test)

X-ray Radiographic Inspection: ⅠDegree

Reference Current (AC, DC+)
Electrode Diameter(mm)
φ2.5
φ3.2
φ4.0
φ5.0
Welding Current (A)
60~100
80~140
110~210
160~230

Instructions:
1.The electrodes must be baked under 300~350℃ for an hour before welding and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before welding.
3.When welding, short arc must be used and stringer bead is suitable.