E8015-C1

E8015-C1
Product name : E8015-C1
Item : W707Ni
Details :
 

W707Ni

According with GB E5515-C1
Corresponding with AWS  E8015-C1


Introduction: W707Ni is a kind of low temperature steel electrode containing Ni with low-hydrogen natrium type coating. DCRP (Direct Current Reversed Polarity). All-position welding. The weld metal still has excellent impact toughness under -70℃.


Uses: Used for welding low temperature steel structures under -70℃, such as 09Mn2V, 06MnVAl, 3.5Ni, etc.


Chemical Composition of Deposited Metal (%)
Chemical Composition
C
Mn
Si
S
P
Ni
Guarantee Value
≤0.12
≤1.25
≤0.60
≤0.035
≤0.035
2.00~2.75

Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReL或Rp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥540
≥440
≥17
≥27(-70℃)

Diffusible Hydrogen Content in Deposited Metal: ≤6.0ml/100g(Glycerine Hydrogen Test)

X-ray Radiographic Inspection: ⅠDegree

Reference Current (DC+)
Electrode Diameter(mm)
φ2.0
φ2.5
φ3.2
φ4.0
φ5.0
Welding Current (A)
40~70
60~90
90~120
140~180
170~210

Instructions:
1.The electrodes must be baked under about 350℃ for an hour before welding, and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before welding.
3.When welding, short arc must be used and stringer bead is suitable.